TROPICAL
Hardness : 20 - 25 HRC
Hard Surfacing

Oxidation welding wire Titania martensite type suitable for building material and as a buffer layer under the metal harder.....

TROPICAL
Hardness : 30 - 35 HRC
Hard Surfacing

Titania oxide wires that have welding skills are very good. Results can dibubut welding. Suitable for gear teeth, Sporket, ....

TROPICAL
Hardness : 40 - 45 HRC
Hard Surfacing

Oxidation Titania welding wire which produces a deposit las chrom manganese alloys are very hard to resist crash deformation....

TROPICAL
Hardness : 50 - 52 HRC
Hard Surfacing

Welding wire for treating hard surfaces knife, blade, mortar, and dies.

TROPICAL
Hardness : 58 - 60 HRC
Hard Surfacing

Welding wire for treating hard surfaces cutters, drills, knives, blades, mortar and dies.

TROPICAL
Hardness : 56 - 59 HRC
Hard Surfacing

Welding wire special hard surface to coat cutting tools, knives, blades, hammers and grinders oil palm seeds, bolts - bolts etc....

TROPICAL
Hardness : 59 - 62 HRC
Hard Surfacing

Hard surface welding wire for tractors and equipment - towing equipment, digger teeth, hammer destroyer and scraper blade. It....

TROPICAL
Hardness : 60 - 62 HRC
Hard Surfacing

Welding wire is very thick to coat the parts - parts or components - components that are exposed to severe abrasion as grinding....

TROPICAL
Hardness : 62 - 65 HRC
Hard Surfacing

Hard surface welding wire with low hydrogen to weld on AC / DC. Suitable for welding components affected by severe abrasion and....

TROPICAL
AWS : E-Mn-Ni
Manganese Steel

Wire welding with high manganese used to coat and to connect such Mn steel rails and other steel string.

TROPICAL

Sugar Rod

Welding wire which produces a heavy layer of weld metal austenite structure bearing metal carbide. Results lasnya withstand high loads with abrasion....

Full austenite welding wire to connect the material - the material difficult to weld. Weld metal is very ductile and can absorb shock loads. Suitable for use as a buffer layer for....

Welding wire Titania mixed oxides with stainless steel weld metal austenite Cr/ 13% 23% Ni. Content of the alloy and high-level ferrit mild steel capable of connecting with low....

Welding wire Titania mixed oxides type austenite stainless steel with Cr/ 12% 23% Ni/ 2.5% Mo. Content of the alloy and high-level cross ferrit metal caused by welding is easy to....

Titania oxide welding wire specifically for the welding of austenite stainless steel filled with 25% Cr/ 20% Ni, type 310, used for corrosion resistance and oxidation at....

Titania oxide welding wire with a deposit of 29% Cr / 9% Ni type stainless steel austenite-ferrit. Used for welding high carbon hard equipment, dies and steel springs, 13% Mn....

Titania oxide welding wire for welding low-carbon materials, molybdenum alloys, 316 austenite stainless steel and acid resistant 316L plate. Welding angle produces a smooth....

Titania oxide welding wire for welding steel yield Cr/ 13% 19% Ni/ 3.5% Mo. This type is used where corrosion resistance is required higher than 316 L. Higher Mo content of this....

THIS WELDING ALLOYS IS SPECIALLY DESIGNED FOR TROPICAL COUNTRIES WITH HUMIDITI

Welding wire Titania mixed oxides with Nb stable for welding the same with the composition of 18% Cr/ 10% Ni austenite type stainless steel with Nb or Ti is stable 347 and 321....